 TA2 Industrial - Pure Titanium Titanium Rod  1,Products:  TA2 industrial pure titanium (non - alloyed) has a medium strength, with a typical yield strength of 351 Mpa.  TA2 industrial pure titanium features excellent corrosion resistance, good ductility and formability. It can be cold - formed and also has good   weldability. The presence of iron and oxygen contributes to its high strength and formability.  TA2 industrial pure titanium is a versatile metallic material and is very popular in applications where weight reduction is required without   sacrificing overall strength.  2,Application Areas:  Materials used in aerospace, automotive and new energy, industrial molds and dies, and semiconductor fields

Unique Advantages	Main Applications	Execution Standards
1. Excellent corrosion resistance	1. Medical components	GB/T 2965
2. Excellent welding performance	2.Chemical components	-
3.Good formability	3.Marine components	-
4. Good strength-to-weight ratio	4.Aerospace components	-

   4,Technical Parameters

Chemical Composition (Mass Fraction) / %
Element	Ti	Al	V	Fe	C	N	H	O	Other Single	Other Total
Minimum	Balance
Maximum	Balance			0.3	0.1	0.05	0.015	0.25	0.1	0.4

Room Temperature Tensile Properties		High Temperature Mechanical Properties
Minimum	Minimum
Tensile Strength (Rm) / MPa	440	Tensile Strength (Rm) / MPa	--
Yield Strength (Rp0.2) / MPa	320	Test Stress (σ) / MPa	-
Elongation after Fracture (A) / %	18	Test Time (t) / h	-
Reduction of Area (Z) / %	30	Test Temperature / ℃	-

     5,Product Showcase         6,Mechanical/Mechanical Properties of Titanium and Titanium Alloy Plates

Alloy	Condition	Thickness Range/mm	Tensile Strength (Rm)/MPa	Yield Strength (Rp0.2)/MPa	Elongation after Fracture /% ≥	Bending Radius
TA2	M	0.3 - 1.0	440 - 620	≥320	≥35	≥100°, 3t
		> 1.0 - 2.0	440 - 620	≥320	≥30	≥100°, 3t
		> 2 - 5.0	440 - 620	≥320	≥25	≥90°, 3t
		> 5 - 10.0	440 - 620	≥320	≥25	-
		> 10.0 - 30	440 - 620	≥320	≥18	-
TC4	M	0.5 - 1.8	925 - 1150	≥870	≥12	≥105°, 9t
		> 1.8 - 4.0	925 - 1150	≥870	≥12	≥105°, 10t
		> 4.0 - 5.0	925 - 1150	≥870	≥10	≥105°, 10t
		> 5.0 - 10.0	925 - 1150	≥825	≥10	-
		> 10.0 - 100	925 - 1150	≥825	≥9	-

Alloy	Condition	Thickness Range/mm	Tensile Strength (Rm)/MPa	Test Temperature/℃	Test Stress(σ)/MPa	Test Time(t)/h
TC4	M	0.5 - 30.0mm	≥590	400	540	≥100
			≥540	500	195